%0 Journal Article %T Additive Manufacturing and Vulcanization of Natural and Synthetic Rubbers %A Leineweber, Sebastian %A Reitz, Birger %A Overmeyer, Ludger %A Sundermann, Lion %A Klie, Benjamin %A Giese, Ulrich %J Logistics Journal : Proceedings %D 2022 %V 2022 %N 18 %@ 2192-9084 %F leineweber2022 %X Additive manufacturing of thermoplastics and metals is a sustainable and established process in industry for the rapid production of individual technical components. For a long time, this technology was not accessible for the group of elastomers, or only to a limited extent in the form of thermoplastic elastomers or silicone rubbers. The development of the Additive Manufacturing of Elastomers (AME)-process has enabled the additive manufacturing of high viscosity rubbers. In future, additively manufactured rubber components may be used in technical logistics in particular. On the one hand, the supply of spare parts such as sealing and damping elements is possible, and on the other hand, the production of individual geometries for grippers in handling technology. For the additive manufacturing of rubber, an industrial 3D-printer was modified by a twin screw extruder, which can process rubber filament and deposit it on a printing plate in strand form, similar to the thermoplastic Fused Filament Fabrication (FFF)-process. The use of a screw extruder is necessary because the viscosity of the rubber does not decrease sufficiently with heating, making it impossible to guide the filament through conventional print heads for thermoplastic filaments. The AME-process is a two-step manufacturing process. First, the components are additively manufactured, followed by vulcanization in a high-pressure autoclave or heating oven. Single-part production is a particular challenge in this case, as the vulcanization time depends on the rubber compound and the component geometry. In order to avoid waste, it is therefore necessary to know the optimum vulcanization time before vulcanization. For this purpose, a simulation was developed and validated that outputs the degree of crosslinking in the component as a function of the vulcanization temperature and time. %L 620 %K Additive Fertigung %K Kautschuk %K Vulkanisation %K Wärmeübertragung %K Zugversuche %K additive manufacturing %K heat transfer %K rubber %K tensile testing %K vulcanization %R 10.2195/lj_proc_leineweber_de_202211_01 %U http://nbn-resolving.de/urn:nbn:de:0009-14-55928 %U http://dx.doi.org/10.2195/lj_proc_leineweber_de_202211_01